Maha Cement-OPC 53 grade
Maha – OPC 53 grade
cement, is a high strength, best quality cement designed to suit the modern
construction practices. It is manufactured with excellent quality clinker,
containing high percentage (56-60%) of Tri-calcium Silicate (C3S), and optimum
quantity of gypsum. This cement is ideal for designing high strength, high
performance concrete used in high rise buildings, bridges, flyovers,
pre-stressed concrete applications, under water concreting, concrete roads etc.
Due to its uniform and consistent 28 days’ compressive strength 60 MPa Maha –
OPC 53 is the most preferred brand by Ready Mix Concrete manufacturers and
infrastructure project engineers.
Please
refer the table below for its typical values as against requirement as per
IS 269-2015
|
Physical
Requirements |
Requirement as
per IS 269 : 2015 |
Maha Cement OPC 53 |
|
|
Fineness |
Specific Surface (m2/kg) |
225(min) |
295 |
|
Setting Time |
a. Initial minutes) |
30
(min) |
165 |
|
b. Final (minutes) |
600
(max) |
240 |
|
|
Soundness |
Expansion of unaerated
cement |
||
|
a. By LeChatelier Method
(mm) |
10
(max) |
1.0 |
|
|
b. By Auto Clave (%) |
0.8
(max) |
0.074 |
|
|
Compressive Strength |
a. 72 ± 1 hr i.e. 3 days (M
Pa) |
27
(min) |
38 |
|
b. 168 ± 2 hr i.e. 7 days (M
Pa) |
37
(min) |
48 |
|
|
c. 672 ± 4 hr i.e. 28 days
(M Pa) |
53
(min) |
60 |
|